CO content 6% Unground Tungsten Carbide round bar fixed length Density 14.8 g / cm3

AIA-1

Send Inquiry

Description

CO content 6% Tungsten Carbide Rod Blanks fixed length, with Density 14.8 g / cm3

?


Description:?

?

Tungsten carbide rod HF06 (K10), a WC-Co alloy, Co content 6%, made up by 0.4μm ultra fine grain carbide powder with superior performance and homogeneous compact structure is produced by Hot Isolation Pressing sintering technique, though which cemented carbide material is fully consolidated by simultaneous application of heat and pressure, leading to a product that contains little or no porosity. Therefore, product quality is stable and reliable, and has long service life.

?

Our carbide rods are sintered by vacuum HIP furnace so that we can guarantee products are with good densification and high transverse rupture strength.

?

Our solid carbide bars can be offered in various sizes. Apart from abundant standard specification in stock, we also accept custom order.?

?

Production process: dosing, wet-milling, pressing, sintering, quality test, finished product, packaging.

?

- ISO Range: K10

?

- with 94% tungsten carbide, 6% cobalt?

?

- Made of 0.4 micron ultrafine TC powder

?

- Hardness: 93.5-93.8 HRA

?

- Bending strength: >3200 MPa

?

- Density:?14.8 g/cm3

?

- As sintered
? ? ? ? ? ? ? ? ? ? ? ? ? ? ? ? ? ? ? ? ? ??
- Standard inch length: unground fixed length

?


Specifications:

?


?

Solid?rods-?cut?to?length(inch):

?

- - - -
D | L | D | L |
?(inch) | (mm) | (inch) | Tol (+1.5 mm) | (inch) | (mm) | (inch) | Tol (+1.5 mm) |
3/16 | 0.188 | 4.763 | 1 1/2 | 1.5 | 38.1 | 3/8 | 0.375 | 9.525 | 2 | 2 | 50.8 |
3/16 | 0.188 | 4.763 | 2 | 2 | 50.8 | 3/8 | 0.375 | 9.525 | 2 1/2 | 2.5 | 63.5 |
3/16 | 0.188 | 4.763 | 2 1/2 | 2.5 | 63.5 | 3/8 | 0.375 | 9.525 | 3 | 3 | 76.2 |
3/16 | 0.188 | 4.763 | 3 | 3 | 76.2 | 3/8 | 0.375 | 9.525 | 3 1/2 | 3.5 | 88.9 |
3/16 | 0.188 | 4.763 | 4 | 4 | 101.6 | 3/8 | 0.375 | 9.525 | 4 | 4 | 101.6 |
1/4 | 0.250 | 6.350 | 1 1/2 | 1.5 | 38.1 | 3/8 | 0.375 | 9.525 | 6 | 6 | 152.4 |
1/4 | 0.250 | 6.350 | 2 | 2 | 50.8 | 1/2 | 0.500 | 12.700 | 2 1/2 | 2.5 | 63.5 |
1/4 | 0.250 | 6.350 | 2 1/2 | 2.5 | 63.5 | 1/2 | 0.500 | 12.700 | 3 | 3 | 76.2 |
1/4 | 0.250 | 6.350 | 3 | 3 | 76.2 | 1/2 | 0.500 | 12.700 | 3 1/2 | 3.5 | 88.9 |
1/4 | 0.250 | 6.350 | 4 | 4 | 101.6 | 1/2 | 0.500 | 12.700 | 4 | 4 | 101.6 |
1/4 | 0.250 | 6.350 | 6 | 6 | 152.4 | 1/2 | 0.500 | 12.700 | 5 | 5 | 127 |
5/16 | 0.313 | 7.938 | 2 | 2 | 50.8 | 3/4 | 0.750 | 19.050 | 3 | 3 | 76.2 |
5/16 | 0.313 | 7.938 | 2 1/2 | 2.5 | 63.5 | 3/4 | 0.750 | 19.050 | 4 | 4 | 101.6 |
5/16 | 0.313 | 7.938 | 3 | 3 | 76.2 | 3/4 | 0.750 | 19.050 | 5 | 5 | 127 |
5/16 | 0.313 | 7.938 | 4 | 4 | 101.6 | 3/4 | 0.750 | 19.050 | 5 1/4 | 5.25 | 133.4 |
5/16 | 0.313 | 7.938 | 6 | 6 | 152.4 | 3/4 | 0.750 | 19.050 | 6 | 6 | 152.4 |
- - - -
?
?
Areas?of?Application:

?

We would be glad to advise you when choosing the grades to suit optimally your requirements. Following are applications that our HF06(K10) fits for cutting.?

?

1. Grey cast Iron
2. Unalloyed steels
3. Plastic

?

?

Competitive Advantage:

?

Compared to high speed steel, tungsten carbide consists of natural hard and stable phase, and practically doesn’t lose any level of its high hardness when heating up. However, the high hardness of HSS is only in a result of quenching process during which hard phase nucleates & grows. It breaks down easily when annealing. Therefore, carbide tools last significantly longer than HSS. ?
? ??
Our products range from tungsten powder, tungsten carbide powder to cemented carbide rod. About our powder, 11 years are accumulated to be professional, winning high reputation within China, which indicates every pre-process for making solid rods is clearly monitored. Consequently, the quality of solid TC rods is guaranteed to be high and stable.?